APPROXIMATE SOLIDS CONTENT
64% by weight.
52.5% by volume.
Specific gravity: 1.215 (nominal).
DRYING TIMES
At approx. 20°C. / 50% R.H., 3 hours.
At approx. 3°C., allow up to 24 hours.
PACK SIZES
10 litres & 25 litres.
[ top ]
Decothane
Typical Test Data
T.B. Numbers refer to specific Technical Bulletins which are available on request.
CHEMICAL RESISTANCE
Decothane EC & SP TB 6/EC, 261/DSP
Resistant to a wide range of reagents including paraffin, petrol, fuel oil, white spirit, acid rain, detergents and moderate solutions of acids and alkalis. Some low molecular weight alcohols can soften.
Salt spray to BS.3900 Part F4 and ASTM B117 - 1000 hours
No rusting, blistering or delamination. TB 361/EC, 262/DSP
Decothane Clearglaze
Resistant to standard 10% solutions of mineral acids, most alkalis, acid rain and detergents. Some oils and solvents may soften surface.
Salt spray to BS.3900 Part F4 and ASTM B117 - 500 hours
No rusting, blistering or delamination.
APPROXIMATE SOLIDS CONTENT
Decothane EC: 83.6% by weight; 76.9% by volume.
Specific gravity: 1.34
Decothane SP: 86.8% by weight; 80.4% by volume.
Specific gravity: 1.45
Decothane Clearglaze: 64.9% by weight; 59.6% by volume.
Specific gravity: 1.033
DRYING TIMES
Decothane EC
At approx. 20ºC. / 50% R.H., touch dry at 2 hours 45 minutes; through cure at 5 hours.TB 360/EC
At 2ºC, allow overnight curing before applying Decothane SP.
Decothane SP
At approx. 20ºC. / 50% R.H., touch dry at 2 hours; through cure at 5 hours. TB 259/DSP
At approx. 2ºC., touch dry overnight; through cure at 24 hours.
Decothane Clearglaze
At approx. 20ºC. / 50% R.H., touch dry at 6 to 7 hours; through cure at 8 hours.
At approx. 2ºC., through cure at 24 hours.
PACK SIZES
Decothane EC: 12.5 litres & 25 litres.
Decothane SP: 12.5 litres & 25 litres.
Decothane Clearglaze: 5 litres & 25 litres.
[ top ]
Soladex
Typical Test Data
T.B. Numbers refer to specific Technical Bulletins which are available on request.
TYPICAL DRY FILM THICKNESS
450 microns (unreinforced).
FIRE RESISTANCE
BS.476 Part 3
Class FAA rating on foam. TB 162/SLX, 163/SLX
BS.476 Part 7
Class 1 rating on asbestos cement. TB 161/SLX
CHEMICAL RESISTANCE
Highly resistant to acids and alkalis. TB 6/SLX
Salt spray - BS.3900 Part F4 - 5000 hours TB 172/SLX
Soladex over LPL Epoxy Metal Primer; no effect.
Prohesion - ASTM G85-94 - 5000 hours
Soladex over LPL Aqueous Metal Primer; no effect.
APPROXIMATE SOLIDS CONTENT
41.3% by weight.
27.2% by volume.
Specific gravity: 1.10
DRYING TIMES
At approx 20ºC. / 50% R.H., touch dry at 2 to 3 hours; through cure at 8 hours.
At approx 3ºC., touch dry overnight; through cure at 24 hours.
Resistance to rain damage is almost immediate.
PACK SIZES
5 litres & 25 litres.
For details of Soladex systems, please consult our Technical Sales Department.
[ top ]
Isoclad
Typical Test Data
T.B. Numbers refer to specific Technical Bulletins which are available on request.
TYPICAL DRY FILM THICKNESS
700 microns.
TENSILE ELONGATION
150%
FIRE RESISTANCE
Complies with BS.476 Part 3 (SAA).
CHEMICAL RESISTANCE
Resistant to standard 10% solutions of acids and alkalis. TB 6/IA
Salt spray - BS.3900 Part F4 - 4000 hours TB 8/I
No effect.
Prohesion - ASTM G85-94 - 5000 hours
No effect.
APPROXIMATE SOLIDS CONTENT
62% by weight.
51.1% by volume.
Specific gravity: 1.215
DRYING TIMES
At approx. 20ºC. / 50% R.H., 3 hours.
At approx. 3ºC., allow up to 24 hours.
PACK SIZES
10 litres & 25 litres.
For details of Isoclad systems, please consult our Technical Sales Department.
[ top ]
Reemat Flexitape Systems
SIZES
Light Duty Flexitape 5 cm. & 15 cm. wide rolls; 50 metre lengths.
Heavy Duty Flexitape 7.5 cm. & 15 cm. wide rolls; 50 metre lengths.
[ top ]
Reemat Glass Fibre Mats (GFM) Systems
SIZES
Reemat Standard 1 metre wide roll; 200 metre lengths; total area = 200m².
Reemat Premium 1.3 metre wide roll; 155 metre lengths; total area = approx. 200 m².
[ top ]
Disclaimer: The information contained herein is correct to the best of our knowledge, but it does not necessarily refer to the particular requirements of the customer. If the customer has any particular requirements, it should make them known in writing to Liquid Plastics, and obtain further advice accordingly.